NodularIron&GrayIron球墨铸铁与灰铸球墨铸铁预处理技术原理及生产应用实例铁陈子华（福士科铸造材料（中国）有限公司，上海200050）摘要：介绍了预处理技术提高球铁冶金质量（包括细化石墨球、增加石墨球数、提高球化率、改善铁液流动性和降低球铁件缩松、缩孔倾向）的基本原理；强调了其应用要点在于预处理反应Ba+O→BaO、Ba+S→BaS、La+S→LaS须在球化反应前进行，才能达到为铁液球化提供良好基础的目的；用高质量厚大球铁件和薄壁球铁件的生产实例说明了预处理技术的优势所在。关键词：球墨铸铁；预处理；原理；应用中图分类号：TG255文献标识码：B文章编号：1003-8345（2010）05-0031-06DOI：10.3969/j.issn.1003-8345.2010.05.004PrincipleandProductiveApplicationExamplesofPretreatmentTechniqueUsedforNodularIronsCHENZi-hua（FOSECOFoundryMaterials（China）Co.Ltd.,Shanghai200050，China）Abstract:Thebasicprincipleofpretreatmenttechniqueusedtoimprovemetallurgicalqualitiesofnodularironswasintroducedincludingtherefinementofthegraphitenodules,increaseofnodulargraphitecount,improvementofnodularity,improvementofflowabilityoftheironmelt,aswellasdecreaseofshrinkagetendencyofnodularironcastings.ItwasstressedthatthekeypointofitsapplicationwastoensurethepretreatingreactionssuchasBa+O→BaO、Ba+S→BaS、La+S→LaStooccurandfinishbeforethenodularizingreactionwiththepurposetocreateagoodbaseforthenodularizationoftheliquidiron.Somehighqualityandheavysectionnodularironcastingsweretakenasexampletoshowtheadvantagesofthepretreatmenttechnique.Keywords：nodularcastiron;pretreatment;principle;appilication生产球铁件时，在球化处理前先对铁液进行对其正确应用提供参考。预处理将对提高铁液冶金质量产生极为有益的预处理技术的概念作用，因而，近年来，人们越来越关注该技术的发1展和应用情况，笔者在此作一简单介绍，以期能1．1传统的预处理工艺传统上，对铁液的预处理包括利用SiC、FeSi收稿日期：2009-12-20修定日期：2010-07-15或增碳剂等添加剂进行的处理，其目的是改善铁作者简介：陈子华（1971-），男，主要负责中国区市场的技术支持工作。液的性能，增加单位面积的形核核心，降低铁液→→→→→→→→→→→→→→→→→→→→→→→→→→→→→→→→→→→→→→→→→→→w（Al）量，对铸铁蠕化率高低并无明显影响；66.（）（5）对于上述蠕化剂，在处理温度和加入量[2]JOperTimothy.MetalsHandbookvol.8[M].GenevaSwitzerland，1973：360.相同条件下，铁液的CE超过4.3%时，金相组织[3]子澍，杨长江，陈桂馨，等.用冲天炉高硫铁液制造蠕墨铸铁齿中明显出现球状石墨，蠕化率将降低。轮的试验[J].现代铸铁，2008，（3）：56-62.（编辑：王峰，E-mail：xdzt_wf@fawfc.com）参考文献（编审：袁亚娟，E-mail：xdzt－yyj@126.com）[1]东北工学院.铸铁及其熔炼[M].北京：北京冶金出版社，1978：2010/5现代铸铁31球NodularIron&GrayIron墨铸铁与灰的过冷度。通常的做法是：在出铁前5～10min，在致，造成两种铁液的w（O）量一个为20ppm，一铸铁炉内加入SiC或石墨质增碳剂，加入量为0.1%～个为120ppm，