兼顾热轧工艺润滑的工作辊磨损预报模型)))邵健何安瑞杨荃等兼顾热轧工艺润滑的工作辊磨损预报模型1112邵健何安瑞杨荃郭宏伟1.北京科技大学高效轧制国家工程研究中心,北京,1000832.济南钢铁集团公司热轧厂,济南,250101摘要:通过对某1700热连轧厂润滑轧制中轧辊磨损主要影响因素的研究,提出了包含润滑项的工作辊磨损预报模型,并采用模拟退火遗传算法估算模型主要参数。现场运用结果表明,该工作辊磨损模型结构及其模型参数能够兼顾热轧润滑和非润滑工况,提高了工作辊磨损的预报精度,满足在线运用需求。关键词:热轧;工作辊磨损;润滑;板形控制;自由规程轧制中图分类号:TG333.1文章编号:1004)132X(2009)03)0361)04WorkRollWearPredictionModelTakinginAccountLubricationinHotRollingShaoJian1HeAnrui1YangQuan1GuoHongwei21.NationalEngineeringResearchCenterforAdvancedRollingTechnology,UniversityofScienceandTechnologyBejing,Beijing,1000832.HotStripMillPlantofJinanIronandSteelCompany,Jinan,250201Abstract:Basedonmaininfluencefactorsofrollwearinlubricationrollinginacertain1700hotstripmill,thispaperproposedaworkrollwearpredictionmodelincludinglubricationfactor,andesti2matedkeyparametersusingsimulatedannealinggeneticalgorithms.Theonsitetestresultsshowthatthemodelstructureofworkrollwearandmodelparameterscancatertonon-lubricationrollingandlubricationrollingconditions,andimprovewearpredictionaccuracyofworkrolltomeettherequire2mentsofonlineuse.Keywords:hotrolling;workrollwear;lubrication;profileandflatnesscontrol;schedulefreerolling0引言工作辊磨损预报模型进行修正,通常采用以下两热轧工艺润滑的实施可以减小轧辊磨损、降种方法:¹在现有磨损预报模型基础上乘以适当低能耗,为实现自由规程轧制提供有利条件。工的修正系数得到润滑轧制中工作辊磨损值;º收作辊磨损预报模型作为板形设定计算的核心,影集多组润滑轧制实测磨损数据,重新回归工作辊响着设定计算的精度。工作辊磨损预报模型一直磨损模型系数。不管是方法¹还是方法º,模型是研究的热点和难点,而润滑轧制引入无疑又增结构均不能从定量上反映不同润滑条件对工作辊加了研究的难度。目前工业轧机在线使用的磨损磨损的改善程度。预报模型均只考虑了磨损的几个最主要参数[1],表1为济钢1700热连轧厂实施润滑轧制以如轧制力、带钢宽度、接触弧长、轧制单位长度,而后F6机架工作辊磨损实测值和预报值的比较,把一些不确定因素如润滑条件、轧辊材质、氧化铁润滑轧制引入后,磨损模型采用方法¹进行预报皮特性、温度等用某一系数表示,如果轧制过程中修正。从表1可以看出,由于不同轧制单位之间不确定因素自身特性变化较大,则磨损模型预报工艺参数差别较大,运用同样的修正值不能精确精度就会降低。由于润滑条件受众多轧制工艺参预报工作辊磨损。数影响,因此有必要定量分析热轧工艺润滑对磨表1不同润滑轧制单位磨损实测值与预报值损的改善。F6上辊F6下辊F6中点轧制主轧规格中点磨损中点磨损磨损预报误差1实施工艺润滑后轧辊磨损模型的常用单位(mm)测量半径测量半径半径值(%)值(Lm)值(Lm)(Lm)处理方法SPHC(1010@3,3.5,4)1978215140.7SPHC(1210@3.5)工业轧机实施润滑轧制后,需对在线使用的SPHC(1270@3,3.5,4)收稿日期:2008)03)04213412916620.7SPHC(1250@2.75)基金项目:/十一五0国家科技支撑计划项目(2006BAE03A13)#361#中国