年第期中国非金属矿工业导刊总第期2009477【加工技术及设备】气流粉碎机制备超细膨润土试验研究卢福宁1，林美群2，莫伟2(1.广西大学实验设备处，广西南宁530004；2.广西大学资源与冶金学院，广西南宁530004)摘要：本文采用气流粉碎机进行膨润土超细粉体制备研究，主要考察设备操作参数对该粉体制备效果的影响。结果表明，增大给料速度并不利于膨润土粉碎中粒径的减少；而增大粉碎压力则反之；并且加料压力对膨润土粉碎粒径的影响均较前两者小。通过XRD及IR分析得知粉碎过程中机械力作用使得膨润土晶体结构发生一定变化，从而会引起其物化性能的改变。关键词：膨润土；超细粉碎；气流粉碎机中图分类号：P619.255;TD985文献标识码：A文章编号：1007-9386(2009)04-0044-03StudyonPreparationofUltra-fineBentonitebyJetMillLuFuning1,LinMeiqun2,MoWei2(1.EquipmentManagementDepartmentofGuangxiUniversity,Nanning530004,China;2.CollegeofResourcesandMetallurgyofGuangxiUniversity,Nanning530004,China)Abstract:Thepaperadoptedajetmilltoprepareultra-finebentonite,andmainlyseekintotheeffectofequipmentoperatingparametersonbentonitepulverized.Theresultshowedthatincreasingfeedingratewentagainstthereducingtheparticlesizeofbentonite,onthecontrary,increasingthecrushingpresswashelpfultothatofbentonite.Andthefeedingpresshaddonelesseffectwhencomparingwithfeedingrateandcrushingpress.ItcouldbelearnthatthecrystalstructureofbentonitewouldchangeduringthecrushingprocessunderthemechanicalforcethroughXRDandIRanalyzing,whichwouldresulttothechangeofthephysicalandchemicalpropertiesofbentonite.Keywords:bentonite;ultrafinegrinding;jetmill膨润土又称膨土岩、斑脱岩，是一种以蒙脱石为构和物化性能的影响。主要矿物的粘土岩。一直以来膨润土以其优异的抗渗1材料与方法性、粘结性、膨胀性、吸附性及阳离子交换性等特殊1.1试验原料性能在国际上被广泛应用于地下防水、污水处理、荒试验用膨润土为广西宁明膨润土，矿石呈灰色，漠治理及石油、冶金、轻工、纺织、农业、医药、食土状光泽，密度为1.75～2.23×103kg/m3，具滑品、日化等多方面，被称为“万用粘土”。近年来，感，吸水缓慢膨胀呈糊状，主要化学成分(%)为：纳米膨润土产品在化妆品、光催化剂载体和聚合物/SiO265，Al2O319、Fe2O36.7、MgO3.1、CaO1.9、粘土纳米复合材料方面的应用研究日益引起国内外众K2O1.6、Na2O0.9。多学者的普遍关注，与此同时，人们对膨润土矿物原图1及表1为所取样品的粒度组成测定结果，分析料产品细度亦提出了更高要求，即膨润土产品的利用可知，膨润土原土颗粒粒度分布的有关特征尺寸(μm)粒度达到微米甚至亚微米级别。分别为：d103.655、d5017.169，d9047.809。机械粉碎是实现膨润土颗粒细化的重要手段，常8规方法是膨润土原矿经干燥处理后利用雷蒙磨或球磨6获得其粉化产品，然而采用气流粉碎机进行膨润土超(%)4细粉碎方面的研究鲜见报道。气流粉碎机是最常用的体积超细粉碎设备之一，气流粉碎的产品除了粒度细以2外，还具有粒度分布较窄、颗粒表面光滑、颗粒形状00.010.111010010003000规则、纯度高、活性大、分散性好等特点[1]。因此本粒度(μm)文采用气流粉碎机进行膨润土超细粉体制备研究，主图1膨润土样品的粒度分布要考察设备操作参数对该粉体制备效果的影响，并通1.2超细粉碎设备过XRD、IR等测试手段分析了粉碎