2000年8月化学工业与工程第17卷第4期Aug.2000CHEMICALINDUSTRYANDENGINEERINGVol.17No.4研究简报环氧2丙烯酸阴极电泳涂料的实验研究()——合成工艺和配方周子鹄,涂伟萍,杨卓如,陈焕钦(华南理工大学化工所,广东广州510640)摘要:本文详细地研究了环氧树脂为母体,丙烯酸类单体接枝共聚物组成的自交联阴极电泳涂料的配方和合成工艺条件,确定了环氧树脂的环氧值、丙烯酸单体配比、接枝共聚反应温度与时间及有机胺等因素,同时探讨了它们对树脂及漆膜性能的影响。关键词:环氧树脂;丙烯酸;阴极电泳涂料;自交联中图分类号:TQ63011文献标识码:B文章编号:100429533(2000)0420235205TheExperimentalResearchofEpoxy-AcrylicCathodicElectrodepositionCoatingZHOUZi2hu,TUWei2ping,YANGZhuo2ru,CHENHuan2qin(ResearchInstituteofChemicalEngineering,SouthChinaUniversityofTechnology,GuangdongGuangzhou510640,China)Abstract:Inthispaperdetailresearchontheformulaandsynthetictechnologyconditionsofself2crosslinkingcathodicelectrodepositioncoatingwasmade,whichbasedonepoxyresinasthematrixwithacrylicmonomersgraftingandcopolymerization.Thefactorscontainingtheepoxyvalue,ratiosofacrylicmonomers,temperatureandtimeofcopolymerizationreactionaswellasorganicamineweredetermined.Theeffectsoftheconditionsonthepropertiesofresinandfilmwerediscussed.Keywords:epoxyresin;acrylic;cathodicelectrodepostioncoating;self2crosslinking收稿日期:1999205231作者简介:周子鹄(19742),男,湖南邵东人,华南理工大学化工所博士生,主要从事涂料树脂的合成研究。©1995-2005TsinghuaTongfangOpticalDiscCo.,Ltd.Allrightsreserved.632化学工业与工程2000年8月阴极电泳涂料的发展已有近30年的历表1树脂基本配方史,由于它具有比阳极电泳涂料更优异的防原料用量(质量分数,以%计)腐蚀能力,更高的泳透力,操作方便,尤其不环氧E24270～80污染环境等特点,已广泛应用于汽车、电器具甲基丙烯酸甲酯8～13及建材等领域。阴极电泳涂料发展很快,品种丙烯酸丁酯5～7繁多,目前国际上普遍采用的主要有两大体苯乙烯5～7系:美国PPG公司的双组分水乳型体系和德甲基丙烯酸胺2国Hoechsts公司的单组分水溶型体系[1]。为了适用我国涂料工业,特别是汽车涂装的要2)合成工艺:在装有冷凝器、滴液管及温度计求,上海涂料研究所和化工部涂料研究所于的四口烧瓶中,用乙二醇预溶好环氧树脂,然80年代相继研制出阴极电泳涂料,但是因技后滴加甲基丙烯酸甲酯、丙烯酸丁酯、苯乙术和原材料的限制,国内阴极电泳涂料的性烯、甲基丙烯酰胺和BPO的乙二醇溶液,搅能和指标与国外的产品还有相当大的差距,拌下升温至90℃开始反应,在2h内升温到以至于我国许多厂家只好从国外引进阴极电115℃。再补加引发剂BPO,恒温4h,制得共泳涂料生产和涂装技术[2]。聚物的乙二醇溶液。所得的共聚物乙二醇溶环氧2丙烯酸共聚物既具有环氧树脂的液降温至75℃左右,加入二乙醇胺,在100±高模量、高强度、耐化学品性及优良的防腐蚀2℃反应2h,待粘度及胺值等指标合格后,降性;又兼具有丙烯酸树脂的光泽、丰满度、耐温加入醋酸(理论中和量的90%)中和至pH候性好等特点。以其为基料的树脂已在卷材、值518～612后,出料。所得聚合物的粘度罐头、家电、仪表等涂装领域得到广泛的应210s(格氏管,25±1℃),固体分72%(质量用[3]。为此,本文着重研究了环氧2丙烯酸自分数)。取该聚合物100g,加入500g蒸馏水,交联