聚氨酯防水涂料施工方案·【可编辑】【实用文档】doc文档可直接使用可编辑，欢迎下载聚氨酯防水涂料施工方案·【可编辑】目录一、施工准备„„„„„„„„„„„„„„„„„„„„„„1二、操作工艺„„„„„„„„„„„„„„„„„„„„„„2三、质量标准„„„„„„„„„„„„„„„„„„„„„„4四、成品保护„„„„„„„„„„„„„„„„„„„„„„5五、应注意的质量问题„„„„„„„„„„„„„„„„„„5六、质量记录„„„„„„„„„„„„„„„„„„„„„„5七、安全文明施工质量保证措施„„„„„„„„„„„„„„5一、施工准备1、材料及要求（1)聚氨酯防水涂料,应具有出厂合格证及厂家产品的认证文件，并复验以下技术性能.聚氨酯防水涂料,以甲组份及乙组份桶装出厂;甲组份:异氰酸基含量以3.5?0.2,为宜。乙组份：羟基含量以0.7？0.1，为宜。两组份材料应分别保管，存放在室内通风干燥处，储藏期甲组份为6个月，乙组份为12个月，使用时甲组份和乙组份料按1:2的比例配合,形成聚氨酯防水涂料，技术性能指标如下:固体含量:?93,抗拉强度:？0。6MPa延伸率：？300，低温柔度：在-200C绕？20mm圆棒无裂纹耐热度：800C不流淌不透水性:，0。2MPa干燥时间:1，6h（2)辅助材料:磷酸：用于做缓冲剂。二月桂酸二丁基锡:用于做促凝剂.二甲苯或醋酸乙酯：用于稀释和清洗工具。2、主要机具：(1)电动工具:电动搅拌器。1（2）手动工具：搅拌桶、小铁桶、小平铲、塑料或橡胶刮板、滚动刷、毛刷、弹簧秤、消防器材等。3、作业条件：(1)防水层聚氨酯防水涂料冷作业施工，涂刷防水层的基层应按设计要求抹好找平层,要求抹平、压光、坚实平整，不起沙,含水率低于9,，阴阳角处应抹成圆弧角.（2)涂刷防水层前应将涂刷面上的尘土、杂物，残留的灰浆硬块，有突出的部分处理、清扫干净.(3）涂刷聚氨酯防水涂料不得在淋雨的条件下施工，施工的环境温度不应低于50C，操作时严禁烟火。二、操作工艺1、工艺流程:基层清理？涂刷底胶？涂膜防水层施工？做保护层2、基层处理:涂刷防水层施工前,先将基层表面的杂物、砂浆硬块等清扫干净，并用干净的湿布擦一次,经检查基层无不平整、空裂，起砂等缺陷,方可进行下道工序。3、涂刷底胶(相当于冷底子油)：（1）底胶（基层处理剂)配制:先将聚氨酯甲料、乙料和二甲苯以1:1。5:2的比例（重量比）配合搅拌均匀，配好的料在2h内用完。(2)底胶涂刷:将配制好的底胶料，用长把滚刷均匀涂刷在基层表面，涂刷量为0.3Kg/m2左右,涂刷后4h手感不粘时，即可做下道工序。4、涂膜防水层施工:2(1)防水材料配制：聚氨酯按甲料、乙料以1:2的比例(重量比)配合,用电动搅拌器强制搅拌3，5min至充分拌合均匀即可使用。配好的混合料应2h内用完,不可时间过长。(2）附加涂膜层:穿过墙、顶、地的管道根部，钢筋头、地漏、排水口、阴阳角、变形缝及薄弱部位，应在涂膜层大面积施工前，先做好上述部位的增强涂层(附加层）。附加涂层做法：是在涂膜附加层中铺设玻璃纤维布，涂膜操作时用板刷刮涂料驱除气泡，将玻璃纤维布紧密地粘贴在基层上，阴阳角部位一般为条形，管根为块形，三面角，应裁成块形铺设，可多次涂刷涂膜。（3)涂刷第一道涂膜:在前一道涂膜加固层的材料固化并干燥后，应先检查其附加层部位有无残留的气孔或气泡,如没有,既可涂刷第一层涂膜；如有气孔或气泡，则应用橡胶刮板将混合料用力压入气孔，局部再刷涂膜，然后进行第一层涂膜施工。涂刷第一层聚氨酯涂膜防水涂料,可用塑料或橡胶刮板均匀涂刮，力求厚度一致，在1.5mm左右,即用量为1。5kg/m2。(4）涂刮第二道涂膜:第一道涂膜固化后，即可在其上均匀地涂刮第二道涂膜，涂刮方向应与第一道的涂刮方向垂直，涂刮第二道与第一道相间隔时间一般不小于24h，亦不大于72h.(5)涂刮第三、四道涂膜:涂刮方法与第二道涂膜相同，但涂刮方向应与其垂直。3（6）稀撒石喳：在第三道涂膜固化之前，厨房及卫生间在其表面稀撒粒径约2mm的石喳，加强涂膜层与其保护层的粘结作用。5、涂膜保护层:最后一道涂膜固化后,即可根据建筑设计要求的适应形式抹水泥砂浆找平层。三、质量标准1、保证项目:(1)涂膜防水材料及附加层玻璃纤维布必须符合设计和有关标准规定.并有产品合格证、试验报告。（2)涂膜防水层及其局部应加强的变形缝、预埋管件处、阴阳角部位的做法，必须符合设计要求和施工规范的才规定,不得渗漏水。2、基本项目：（1)涂膜防水的基层应牢固，表面洁净，密实平整，阴阳角呈圆弧形，底胶涂层应均匀，无漏涂。（2）附加涂膜层的涂刷方法、搭接、收头应按设计要求，粘结必须牢固，接缝封闭严密，无损伤